Photoluminescence characterization of AlN nanowhiskers

A.S.Vokhmintsev, I.A.Weinstein, D.V.Chaikin, D.M.Spiridonov, Yu.D.Afonin

Ural Federal University, NANOTECH Centre, 19 Mira Str., 620002 Yekaterinburg, Russia

Abstract: 

Photoluminescence (PL) properties of synthesized Al-rich nanowhiskers with diameter 60±20 nm and bulk AlN single crystals were compared at the room temperature. It was found that PL spectra for AlN nanowhiskers were characterized by three components of the Gaussian shape with maximum energy 3.16, 2.90, and 2.55 eV and halfwidth 0.7, 0.4, and 0.7 eV, respectively. It was shown that the same bands - 3.2 and 2.6 eV - were observed in luminescence of the bulk and nanostructured samples. The registered emissions were attributed to electron-optical transitions between donor levels of the ON-, VN-centers and acceptor states of the CN-centers and (ON-VAl)-complexes.

References: 

1. L.Shen, N.Wang, X.Xiao, Mater. Lett., 94, 150 (2013). http://dx.doi.org/10.1016/j.matlet.2012.12.042

2. B.Liu, Y.Bando, A.Wu et al., Nanotechnology, 21, 075708 (2010). http://dx.doi.org/10.1088/0957-4484/21/7/075708

3. S.P.Grabowski, M.Schneider, H.Nienhaus et al., Appl. Phys. Lett., 78, 2503 (2001). http://dx.doi.org/10.1063/1.1367275

4. H.T.Chen, X.L.Wu, X.Xiong et al., J. Phys. D: Appl. Phys., 41, 025101 (2008). http://dx.doi.org/10.1088/0022-3727/41/2/025101

5. X.Hou, C.Yue, A.K.Singh et al., J. Solid State Chem., 183, 963 (2010). http://dx.doi.org/10.1016/j.jssc.2010.02.022

6. Author's certificate No.2106298.

7. E.N.Mokhov, O.V.Avdeev, I.S.Barash et al., J. Cryst. Growth, 281, 93 (2005). http://dx.doi.org/10.1016/j.jcrysgro.2005.03.016

8. J.-M.Maki, I.Makkonen, F.Tuomisto et al., Phys. Rev. B, 84, 081204-1 (2011). http://dx.doi.org/10.1103/PhysRevB.84.081204

9. L.Trinkler, B.Berzina, D.Kasjan et al., J. Phys.:Conf. Ser., 93, 012040 (2007). http://dx.doi.org/10.1088/1742-6596/93/1/012040

10. D.Chen, J.Wang, D.Xu et al., Vacuum, 83, 865 (2009). http://dx.doi.org/10.1016/j.vacuum.2008.09.003

11. A.S.Vokhmintsev, I.A.Weinstein, D.M.Spiridonov, J. Luminescence, 132, 2109 (2012). http://dx.doi.org/10.1016/j.jlumin.2012.03.066

12. A.S.Vokhmintsev, I.A.Weinstein, D.M.Spiridonov, Phys. Stat. Solidi C, 10, 457 (2013). http://dx.doi.org/10.1002/pssc.201200519

13. M.Bickermann, B.M.Epelbaum, O.Filip et al., Phys. Stat. Solidi C, 9, 449 (2012). http://dx.doi.org/10.1002/pssc.201100345

14. I.A.Weinstein, A.S.Vokhmintsev, D.M.Spiridonov, Diam. Relat. Mater., 25, 59 (2012). http://dx.doi.org/10.1016/j.diamond.2012.02.004

15. S.Pacesova, L.Jastrabik, Czechoslovak J. Phys., 29, 913 (1979). http://dx.doi.org/10.1007/BF01596369

16. B.E.Gaddy, Z.Bryan, I.Bryan et al., Appl. Phys. Lett., 103, 161901 (2013). http://dx.doi.org/10.1063/1.4824731

17. L.Trinkler et al., Phys. Stat. Solidi C, 2, 334 (2005). http://dx.doi.org/10.1002/pssc.200460178

Current number: