The effect of heat treatment on the magnetic properties of ZnO:Mn nanocrystals obtained by ultrasonic aerosol pyrolysis
O.Honchar Dnipro National University, 72 Gagarin Ave., 49010 Dnipro, Ukraine
Samples of ZnO:Mn nanocrystals (impurity concentration 2 at.%) were obtained by ultrasonic aerosol pyrolysis and subjected to heat treatment in air at temperatures of 550°C and 850°C, as well as in a gas medium with hydrogen at a temperature of 550°C. The term of the heat treatment was 20 min. The nanocrystal samples were cooled in a flow of nitrogen gas for 15 min. The samples were studied by X-ray phase analysis, EPR, and the magnetic vibration method before and after annealing. The synthesized samples had ferromagnetic properties at room temperature. The specific magnetization of the sample was Ms = 0.028 emu/g. Heat treatment at T = 550°C led to a decrease in the specific magnetization of the samples (Ms = 0.01 emu/g). After heat treatment at T = 850°C, the ferromagnetic properties in the samples disappeared. Ferromagnetic properties of the samples were restored after heat treatment in a gas medium with hydrogen (Ms = 0.023 emu/g). The regularities of the influence of heat treatment regimes on the magnetic properties of ZnO:Mn nanocrystals are explained by a change in both the number and the ratio of intrinsic defects (oxygen vacancies Vo) and impurity Mn2+ ions located in the surface layer of nanocrystals.
1. I.Zutic, J.Fabian, S.C.Erwin, IBM J. Res. Dev., 50, 121 (2006). https://doi.org/10.1147/rd.501.0121 |
||||
2. S.M.Pogorily, S.M.Ryabchenko, A.I.Tovstolitkin, Ukr. J. Phys. Rev., 6, 37 (2010). | ||||
3. T.Dietl, H.Ohno, F.Matsukura et al., J. Science, 287, 1019 (2000). https://doi.org/10.1126/science.287.5455.1019 |
||||
4. J.Zhang, R.Skomski, D.J.Sellmyer, J. Appl. Phys., 97, 10D303 (2005). https://doi.org/10.1063/1.1845858 |
||||
5. P.Sharma, A.Gupta, K.Rao et al., J. Nature Mater., 2, 673 (2003). https://doi.org/10.1038/nmat984 |
||||
6. D.Rubi, J.Fontcuberta, A.Calleja et al., Phys. Rev. B, 75, 155322 (2007). https://doi.org/10.1103/PhysRevB.75.155322 |
||||
7. V.K.Sharma, G.D.Varma, J. Appl. Phys., 102, 056105 (2007). https://doi.org/10.1063/1.2778283 |
||||
8. J.M.D.Coey, M.Venkatesan, C.B.Fitzgerald, J. Nature Mater., 4, 173( 2005). https://doi.org/10.1038/nmat1310 |
||||
9. R.Mukherji, V.Mathur, J. Nano-Electron. Phys., 11, 03039 (2019). https://doi.org/10.21272/jnep.11(3).03039 |
||||
10. S.Chattopadhyay, K.Neogi, A.Sarkar et al., J. Magn. Mag. Mater., 323, 363 (2011). https://doi.org/10.1016/j.jmmm.2010.09.042 |
||||
11. B.B.Straumal, A.A.Mazilkin, S.G.Protasova et al., J. Phys. Rev. B, 79, 155203 (2009). https://doi.org/10.1103/PhysRevB.79.205206 |
||||
12. T.V.Manh, T.L.Phan, B.W.Lee et al., IEEE Trans. Magn., 51, 2400504 (2015). https://doi.org/10.1109/TMAG.2015.2438064 |
||||
13. V.Yu.Vorovsky, A.V.Kovalenko, A.I.Kushnerov et al., J. Functional Materials, 25, 61 (2018). https://doi.org/10.15407/fm25.01.061 |
||||
14. O.V.Kovalenko, M.F.Bulaniy, V.Y.Vorovskiy et al., J. Phys. Electr., 26, 69 ( 2018). https://doi.org/10.15421/331811 |
||||
15. S.C.Tsai, Y.L.Song, C.S.Tsai et al., J. Mater. Sci., 39, 3647 ( 2004). https://doi.org/10.1023/B:JMSC.0000030718.76690.11 |
||||
16. A.S.Vorokh, J. Nanosyst. Phys. Chem. Math., 9, 364 (2018). https://doi.org/10.17586/2220-8054-2018-9-3-364-369 |
||||
17. M.M.Mezdrogina, E.Yu.Danilovskiy, R.V.Kuzmin, J. Semiconductors, 44, 321 (2010)). https://doi.org/10.1134/S1063782610030097 |
||||
18. O.Jayakumar, H.Salunke, R.Kadam et al., J. Nanotechnology, 17, 1278 (2006). https://doi.org/10.1088/0957-4484/17/5/020 |
||||
19. D.Toloman, A.Mesaros, A.Popa et al., J. Alloy. Compd., 551, 502 (2013). https://doi.org/10.1016/j.jallcom.2012.10.183 |
||||
20. H.Zhou, D.M.Hofmann, A.Hofstaetter et al., J. Appl. Phys., 94, 1965 (2003). https://doi.org/10.1063/1.1586986 |
||||
21. A.Layek, G.Mishra, A.Sharma et al., J. Phys. Chem. C, 116, 24757 (2012). https://doi.org/10.1021/jp211613b |
||||
22. D.Ghica, I.D.Vlaicu, M.Stefan et al., J. Sci. Rep., 9, 6894 (2019). https://doi.org/10.1038/s41598-019-43388-z |
||||
23. E.V.Lavrov, F.Herklotz, J.Weber, J. Phys. Rev., 79, 165210 (2009). https://doi.org/10.1103/PhysRevB.79.165210 |
||||
24. D.M.Hoffmann, A.Hofstaetter, F.Leiter et al., J. Phys. Rev. Lett., 88, 045504-1 (2002) https://doi.org/10.1103/PhysRevLett.88.045504 |
||||
25. C.Yanqiang, D.Wu, Q.Xu, J. Appl. Surf. Sci., 271, 421 (2013). https://doi.org/10.1016/j.apsusc.2013.02.009 |
||||
26. S.J.Guan, N.N.Asu, Yu.Zhang et al., Sci. China Tech. Sci., 62 (2019). https://doi.org/10.1007/s11432-018-9451-y |